Toughblend® PA66-1303
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Toughblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uDsQGh_Toughblend-PA66-1303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughblend® Pa66-1303 is a glass fiber reinforced and barium sulphate filled compound provide good mechanical and dimensional stability properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 94.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.2 | % | ASTM D638 |
| Flexural Modulus | 5120 | MPa | ASTM D790 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.00 mm) | 236 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 275 to 280 | °C | |
| Middle Temperature | 280 to 285 | °C | |
| Front Temperature | 285 to 290 | °C | |
| Nozzle Temperature | 290 to 295 | °C | |
| Processing (Melt) Temp | 275 to 295 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3870 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| NEXT SIGNATURE PA6 G33-100 | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT SIGNATURE |
| Baoding 6126 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Elastamax™ XL-2155 | PolyOne Corporation | TPO (POE) | Elastamax™ |
| LNP™ THERMOTUF™ DF004PSI compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOTUF™ |