GELOY™ HRA222F resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uC1Qcz_GELOYHRA222Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GELOY HRA222F is a multi-purpose, chlorine and bromine free flame retardant PC+ASA alloy for injection molding processes. F1 rating according UL746C. Use for exterior/interior electrical applications requiring UV resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2590 | MPa | ASTM D638 |
| -- | 2520 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 59.0 | MPa | ASTM D638 |
| Yield 4 | 63.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/5 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 5 | 66.0 | MPa | ASTM D638 |
| Fracture 6 | 56.0 | MPa | ASTM D638 |
| Fracture | 51.0 | MPa | ISO 527-2/5 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 7 | 4.2 | % | ASTM D638 |
| Yield 8 | 4.3 | % | ASTM D638 |
| Yield | 4.3 | % | ISO 527-2/5 |
| Yield | 4.4 | % | ISO 527-2/50 |
| Fracture 9 | > 100 | % | ASTM D638 |
| Fracture 10 | > 100 | % | ASTM D638 |
| Fracture | > 50 | % | ISO 527-2/5, ISO 527-2/50 |
| Flexural Modulus 11 | 2520 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 12(23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 0°C | 290 | J/m | ASTM D256 |
| 23°C | 390 | J/m | ASTM D256 |
| -30°C 13 | 9.0 | kJ/m² | ISO 180/1A |
| 0°C 14 | 12 | kJ/m² | ISO 180/1A |
| 23°C 15 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 16 | |||
| 0.45 MPa, unannealed, 100 mm span | 99.0 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 88.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ISO 306/A50 |
| -- | 102 | °C | ISO 306/B50 |
| -- | 104 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -30 to 80°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : -30 to 80°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.00 mm) | V-0 | UL 94 | |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 200 - 230 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 230 - 270 | °C | |
| Nozzle Temperature | 220 - 260 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | Type 1, 5.0 mm/min |
| 8 . | Type 1, 50mm/min |
| 9 . | Type 1, 5.0 mm/min |
| 10 . | Type 1, 50mm/min |
| 11 . | 2.0 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemraz 640 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Evoprene™ G 966 | AlphaGary | SEBS | Evoprene™ G |
| Geon™ Vinyl Flexible R8570B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LG PS 25SP(I) | LG Chem Ltd. | PS (GPPS) | LG PS |
| Ingeo™ 6362D | NatureWorks® LLC | PLA | Ingeo™ |