Surlyn® 9950
| Category: | EMAA , Ethylene Methacrylic Acid |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Surlyn® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uBCfBS_Surlyn-9950.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Surlyn® 9950 is a zinc ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 9950 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Ion Type | Zinc |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance - NBS Index | 130 | ASTM D1630 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Freezing Point | |||
| -- | 63 | °C | ASTM D3418 |
| -- | 63 | °C | ISO 3146 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C, Compression Molded 1 | 12.4 | MPa | ASTM D638 |
| Break, 23°C | 28.3 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 490 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 250 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | ASTM D1822 | ||
| -40°C | 662 | kJ/m² | |
| 23°C | 1020 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -100 | °C | ASTM D746 |
| Vicat Softening Temperature | 79.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 87.0 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow (-20 to 32°C) | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (6350 µm) | 18 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 185 to 285 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 282 TFE 15 | RTP Company | Nylon 66 | RTP |
| SABIC® PPcompound 8536 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Etinox® EK-8780 | Ercros, S.A. | PVC, Flexible | Etinox® |
| Generic PBT - Mineral | Generic | PBT | Generic |