LG PS 50IS
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u8yeSG_LG-PS-50IS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG PS 50IS is a high impact polystyrene material,. This product is available in North America, Latin America, Europe or Asia Pacific,. The main characteristics of LG PS 50IS are: flame retardant/rated flame. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 8.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 80 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | ASTM D955 |
| Dimensional Stability | 0.0 | % | ASTM D1042 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 1770 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 26.5 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20mm | 5.0 | % | ASTM D638 |
| Fracture, 3.20mm | 59 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 3.20 mm) | 42.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 59 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 49 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 120 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 87.0 | °C | ASTM D1525 6 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 44 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 4 | UL 746 | |
| 3.00 mm | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | HB | UL 94 | |
| 3.00 mm, ALL | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 190 - 220 | °C | |
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9518H | Chevron Phillips Chemical Company LLC | HDPE, HMW | Marlex® |
| ACCUTECH鈩?HP0339M10CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Argothane® ST-2592-90 | Argotec LLC | TPU, Unspecified | Argothane® |
| OPNYL OP66GF50 | Ovation Polymers Inc. | Nylon 66 | OPNYL |
| Plexiglas® LED 8N LD48 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |