Starex VH-0819
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u8bU3g_Starex-VH-0819.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame-retardant ABS material with the characteristic of high flow that can be used for the exterior material of large TV and OA devices |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 8.8 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 7.8 | g/10 min | ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.45 to 0.65 | % | |
| Across Flow : 3.20 mm | 0.45 to 0.65 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 104 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/50 |
| Break 3 | 38.0 | MPa | ASTM D638 |
| Break | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 10 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2200 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 59.0 | MPa | ASTM D790 |
| -- 8 | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 200 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 170 | J/m | ASTM D256 |
| 23°C 10 | 22 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 78.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 74.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 84.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 84.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 1.80 mm | V-1 | ||
| 2.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 15 HI K2034 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| BJB Polyurethane TC-8772 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Durepol® PBT A3 G30 PRTA011 BT304 MSP | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| Elastollan® C 70 A 10 P 000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| POLYelast TPE R44 T10 | Polykemi AB | PP+EPDM | POLYelast |