Sarlink® TPV 2564
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u7vmIv_Sarlink-TPV-2564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPV 2564 is a thermoplastic vulcanized rubber (TPV) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.938 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 69 | ASTM D2240 | |
| Shaw A, 5 seconds | 64 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 5.04 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 290 | % | ASTM D412 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 23 | % | ASTM D395 |
| 70°C, 22 hr | 36 | % | ASTM D395 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Xenon Weatherometer 4 | |||
| 2000 hrs Xenon per SAE J-1960, Elongation Retention | 78 | % | |
| 2000 hrs Xenon per SAE J-1960, Tensile Retention | 84 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 173 - 213 | °C | |
| Middle Temperature | 179 - 219 | °C | |
| Front Temperature | 184 - 224 | °C | |
| Nozzle Temperature | 190 - 230 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 35.0 - 60.0 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 204 | °C | |
| Cylinder Zone 2 Temp. | 171 - 210 | °C | |
| Cylinder Zone 3 Temp. | 177 - 216 | °C | |
| Cylinder Zone 5 Temp. | 182 - 221 | °C | |
| Die Temperature | 190 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | ISO 1183 |
| 2 . | ISO 37 |
| 3 . | ISO 37 |
| 4 . | Results are for 2564 BLK 111 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® EQ 71 N | Plastcom | LDPE+EVA | SLOVALEN® |
| Asiga® PlasCLEAR | Asiga | Unspecified | Asiga® |
| Halene H F5001 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| EOS PA 2202 black | EOS GmbH | Nylon 12 | EOS |
| LG ABS AF364 | LG Chem Ltd. | ABS | LG ABS |