Starex TF-0957H
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u79wsz_StarexTF0957H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex TF-0957H is a polymethyl methacrylate-acrylic acid product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical appliances. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.40 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.40 | % | ISO 2577 |
| Traffic : 3.20mm | 0.40 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 108 | ASTM D785 | |
| R scale | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 44.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 44.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 40 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 1900 | MPa | ASTM D790 |
| -- 6 | 1900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 68.0 | MPa | ASTM D790 |
| -- 8 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 49 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 49 | J/m | ASTM D256 |
| 23°C 10 | 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 80.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 85.0 86.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | |||
| 3200 µm | 1.7 | % | ASTM D1003 |
| 3200 µm | 1.7 | % | ISO 13468 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM PE 4420 | Ponachem Compound GmbH | HDPE | PONACOM PE |
| NEFTEKHIM PP 9300M | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Elastron® G G400.A90.B | Elastron USA, Inc. | SEBS | Elastron® G |
| LARIPUR® LPR 6515 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| MAJORIS G400 | AD majoris | PP, Unspecified | MAJORIS |