Tecomid® NA40 CR10 BK111
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecomid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u6tokd_Tecomid-NA40-CR10-BK111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6.6, 10% carbon fiber reinforced, black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.1 | % | Internal method |
| Flow direction | 0.30 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | % | ISO 62 |
| Moisture Content | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 235 | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 70.0 - 110 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 100 | MPa |
| Injection instructions |
|---|
| Pre-drying is not necessary for materials in moisture proof closed bags. |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 AR 5 | RTP Company | PEI | RTP |
| Xuye J-700 | Shandong Xuye New Materials Co., Ltd. | CPVC | Xuye |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6105 BR | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Bergamid™ B70 G30 NC213 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| HYBRANCH HP-100 | DIC Corporation | PS (Specialty) | HYBRANCH |