Hostacom X M2 U35
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u6eSX6_Hostacom-X-M2-U35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% mineral filled PP - Copolymer, good stifness toughness balance and UV resistant. Good scratch resistance used for automotive interior. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 16 | g/10 min | |
| 230°C/5.0 kg | 67 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 18.0 | cm³/10min | |
| 230°C/5.0 kg | 78.0 | cm³/10min | |
| Molding Shrinkage | 0.90 to 1.1 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 66.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 2150 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 4.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 56.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fortron® 4184L6 | Celanese Corporation | PPS | Fortron® |
| EOS PA 2200 Balance 1.0 | EOS GmbH | Nylon 12 | EOS |
| Huafon HF-3H80AL | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Leona™ FG170 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| OTECH PVC OF6328-Boot | OTECH Corporation | PVC, Unspecified | OTECH PVC |