AVP™ TLL40CP
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u6UTI5_AVP-TLL40CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AVP™ TLL40CP is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Primary characteristic: high flow. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 38 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.18 mm) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 75 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm, 50.8 mm Span) | 2410 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm, 50.8 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reverse Notch Izod Impact (23°C, 3.18 mm) | 2100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 127 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 16 | hr | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 288 | °C | |
| Nozzle Temperature | 266 to 282 | °C | |
| Processing (Melt) Temp | 271 to 288 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XT-585 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Shandong Aobang TPU-Polyether 98-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyether | Shandong Aobang TPU-Polyether |
| Stirol UPS-0803 E (1s.) | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| Andur AL 95 AP/Curene® 111 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Flontech® FT-COND2-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |