GLAMIDE® TY-181GC
| Category: | Nylon 6 Elast , Polyamide 6 Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u6HZvl_GLAMIDE-TY-181GC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE® TY-181GC is a Polyamide 6 Elastomer (Nylon 6 Elast) product filled with 43% glass fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.46 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 6.0 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.10 to 0.30 | -- | % | |
| 3.00 mm | 0.30 to 0.60 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.80 | -- | % | |
| Equilibrium, 65% RH | 1.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 280 | 240 | MPa | |
| Yield, 23°C | 170 | 115 | MPa | |
| Yield, 80°C | 110 | 84.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 3.6 | 4.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 13000 | 11700 | MPa | |
| 23°C | 9800 | 6000 | MPa | |
| 80°C | 5600 | 4000 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 345 | 288 | MPa | |
| Yield, 23°C | 245 | 160 | MPa | |
| Yield, 80°C | 130 | 87.0 | MPa | |
| Compressive Strength (23°C) | 140 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 170 | 190 | J/m | |
| 23°C | 330 J/m | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 230 | -- | °C | |
| 1.8 MPa, Unannealed | 218 | -- | °C | |
| CLTE - Flow | 2.4E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | 19 | kV/mm | ASTM D149 |
| Arc Resistance | 90.0 | 83.0 | sec | ASTM D495 |
| Comparative Tracking Index | 575 | 575 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 30.0 to 70.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 20YM240 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| SLOVALEN® PC 51 T 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| TRANSMARE® 19HT60-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| COPYLENE® CM010G | Phillips 66 | PP Impact Copolymer | COPYLENE® |
| RTP 399 X 141353 EG | RTP Company | PC | RTP |