OLEFISTA™ QX1219D/QCM292
| Category: | Elastomer, Specialty , Specialty Elastomer |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | OLEFISTA™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u5wDiu_OLEFISTA-QX1219D-QCM292.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OLEFISTA™QX1219D/QCM292 is a Specialty Elastomer material,. This product is available in the Asia-Pacific region,. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | JIS K7112 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation Under Load (120°C) | 1.00 | % | JIS K6723 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 13.0 | MPa | JIS K6251 |
| Tensile Stress (Break) | 16.0 | MPa | JIS K6251 |
| Tensile Elongation (Break) | 200 | % | JIS K6251 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | 130 | % | JIS K7113 |
| Change in Tensile Strain at Break in Air (150°C, 168 hr) | 90 | % | JIS K7113 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | JIS K6723 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (30°C) | 5.0E+13 | ohms·cm | JIS K6723 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 35 | % | JIS K7201 |
| Additional Information |
|---|
| Blend Ratio: QX1219D/QCM292, 100/3Corresponding Standards: PVCC, TUV (2pfg/1169 PV-1F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 GB 20 | RTP Company | PP, Unspecified | RTP |
| Sup-tech A706SH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| Next PPS PPSG40AW-02BK | Next Polymers Ltd. | PPS | Next PPS |
| LNP™ THERMOCOMP™ RF002ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LEXAN™ HPX8R resin | SABIC Innovative Plastics | PC | LEXAN™ |