KRYSTALFLEX™ PE429
| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | KRYSTALFLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u5Ua2b_KRYSTALFLEX-PE429.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KRYSTALFLEX PE429 is a high performance aliphatic polyether film intended for processing by lamination into a range of glass/plastics components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain | 1.93 | MPa | ASTM D412 |
| 300% strain | 8.27 | MPa | ASTM D412 |
| Tensile Strength 2(Yield) | 27.6 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 440 | % | ASTM D412 |
| Tear Strength | 28.9 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -53.9 | °C | DSC |
| Additional Information |
|---|
| Softening Range, TMA: 120 to 255°FTypical Laminating Parameters:Ultimate Temperature: 194 to 230°FUltimate Pressure: 116 to 174 psiSoaking Time: 30 min/0.25 in |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 TFE 10 FR | RTP Company | ABS | RTP |
| ASTAMID™ MB3EG6 | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |
| EnCom F0 ABS 6040 | EnCom, Inc. | ABS | EnCom |
| Iupilon® EGW2010DR 9005 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| MTEGRITY™ LDPE LD120AA | M. Holland Company | LDPE | MTEGRITY™ LDPE |