NYCOA Polyamide 5033 HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u5GKmk_NYCOA-Polyamide-5033-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 5033 HS is a 33% glass fiber reinforced, heat stabilized Nylon 66 resin used for injection molding. It offers an outstanding balance of mechanical properties over standard grades of conventional Nylon 66. NYCOA 5033 HS has been specifically formulated for optimum thermal stability and chemical resistance. This grade is available in UV stable, custom colors, and impact modified grades. Typical applications include pedal brackets and supports, air intake manifolds, radiator end tanks, valve covers, and power tool housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 200 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3 | 8900 | MPa | ASTM D790 |
| Flexural Strength 4 | 260 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 240 | °C | ASTM D648 |
| Melting Temperature | 263 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 266 - 282 | °C | |
| Middle Temperature | 277 - 293 | °C | |
| Front Temperature | 288 - 304 | °C | |
| Nozzle Temperature | 282 - 302 | °C | |
| Processing (Melt) Temp | 288 - 304 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 to 4.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 985 | RTP Company | PSU | RTP |
| ALTECH® PP-B A 2030/150 GF30 CP | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |
| ASI POLYETHYLENE CP 814-01 | A. Schulman Inc. | LLDPE | ASI POLYETHYLENE |
| INLUBE PESGF20TF15 | Infinity LTL Engineered Compounds | PESU | INLUBE |
| LNP™ STAT-KON™ DX05499 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |