Latilub 75/4-05T G/30-V0
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u4OYLG_Latilub-75-4-05T-G-30-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polybutylene Terephtalate (PBT). PTFE. Glass fibres. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimonium trioxide free. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Flow : 2.00 mm | 0.40 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.8 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.18 | ||
| vs. Itself - Static | 0.22 | ||
| Wear Factor | 220 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 725 | °C | |
| 2.00 mm | 725 | °C | |
| Oxygen Index | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE H645 | Dongbu Hannong Chemical | PS (HIPS) | SOLARENE |
| Badamid® LB70 GF15 | Bada AG | Nylon 6 | Badamid® |
| Akulon® K224-G6-FC BK00001 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| DOMAMID® A1-007-V20-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Epoxies, Ect. 10-3008 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |