LNP™ THERMOCOMP™ RF005 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u3hVHN_LNP-THERMOCOMP-RF005-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF005 is a compound based on Nylon 66 resin containing 25% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound RF-1005 Product reorder name: RF005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 | % | |
| Across Flow : 24 hr | 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9100 | MPa | ASTM D638 |
| -- | 8300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 132 | MPa | ASTM D638 |
| Break | 140 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.9 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7240 | MPa | ASTM D790 |
| -- | 8300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 480 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.00 | J | ASTM D3763 |
| -- | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 259 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 246 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 224 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6331NW | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Starglas CF006 | Eurostar Engineering Plastics | TES | Starglas |
| ELASTOSIL® P 7616-160 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| LAPEROS® E473i | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| Karina BLACK PVC COMPOUND -E 817-48/ 1-F-ERYBT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |