Durepol® PBT A3 HL NTLA010 BT314
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Durepol® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u2gSe9_Durepol-PBT-A3-HL-NTLA010-BT314.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT polyester high viscosity, lubricated. Ideal for injection molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 to 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Peak Melting Temperature | 225 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP23-566-1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Styrilic Grade 2020 | Deltech Polymers Corporation | Acrylic (SMMA) | Styrilic |
| Elastollan® 560 A 13 PTSG 000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| POCAN® KU 1-7301 000000 | LANXESS Corporation | PBT | POCAN® |
| LNP™ THERMOCOMP™ DF0046P compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |