Order Products : sales@su-jiao.com
MAJORIS EFR268
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u1qR3m_MAJORIS-EFR268.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EFR268 is a flame retardant with halogen compound and UL 94 VO classification, intended for injection moulding. The product is available in natural (EFR268) but other colours can be provided on request. APPLICATIONS EFR268 is intended for the injection moulding of electrical component such as:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 125 | °C | ISO 75-2/B |
| Ball Pressure Test (115°C) | Pass | NF C 61-303 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm, 3.0 sec | 960 | °C | IEC 60695-2-13 |
| 2.00 mm, 3.0 sec | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PULSE™ 2013 | Trinseo | PC+ABS | PULSE™ |
| Kemcor HD 6095 Film | Qenos Pty Ltd | HDPE, MMW | Kemcor |
| LIHAN® A706SH | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| Karina GREENY BROWN (SP31456) -E 36/210-GEN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ DF008ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |