InnoTooling™ IE-644-08
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTooling™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u1g2NP_InnoTooling-IE-644-08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-644-08 is a tough, impact resistant elastomer formulated for room temperature hand-batch systems. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury or MOCA. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.16 | g/cm³ | |
| Base Resin | 1.16 | g/cm³ | |
| Hardener | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 621 | MPa | ASTM D790 |
| Flexural Strength | 31.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 58 Mix Ratio by Weight: 60 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 240 to 480 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.18 | Pa·s | |
| 25°C 2 | 1.6 | Pa·s | |
| 25°C 3 | 4.5 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 14 to 18 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 57 to 67 | ASTM D2240 | |
| Tensile Strength | 31.0 | MPa | ASTM D638 |
| Tensile Elongation at Break | 20 | % | ASTM D638 |
| Tear Strength | 74.4 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 3371 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Xuchuan XWB-3360 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Baydur® 426 IMR (Continuous Filament Mat) | Covestro - PUR | PUR-MDI | Baydur® |
| EVICOM™ VN225/3 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| Ebalta GH 707 / BR | Ebalta Kunststoff GmbH | Epoxy | Ebalta |