TECHNYL® C 218 V18 BLACK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u1dGeg_TECHNYLC218V18BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 218 V18 Black is a polyamide 6, heat stabilized, reinforced with 18% of glass fiber, for injection moulding. The product offers an excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.24 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6900 | 3400 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 140 | 75.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 4.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6800 | 3300 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.0 | 16 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 180 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | -- | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.80 | 4.50 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.6 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.6 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 - 235 | °C | |
| Middle Temperature | 235 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86019-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEXUS PE HDPE-1252 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| Ferro PP LPP10BK72NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hostacom X M2 T28 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| POCAN® TS 3221 901510 | LANXESS GmbH | PBT+PET | POCAN® |