CYCOM® PR 520 RTM

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Cytec Industries Inc.
Trademark:	CYCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	u1ZfY0_CYCOM-PR-520-RTM.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
CYCOM® PR 520 RTM is a one-part, 180°C (355°F) curing epoxy resin system offering superior damage tolerance and good strain to failure required for composite primary structure applications. The value of resin infusion is the ability to design complex geometric parts while leveraging a unitized structure which ultimately leads to a reduction in weight, lower part counts and the elimination of many post-manufacturing processes. CYCOM PR 520 RTM is an off-white thick paste at room temperature reducing to a low viscosity when heated for injection. The resin has a low enough viscosity to allow injection at 90 - 100°C (194 - 212°F). Following injection, the resin viscosity decreases with increasing tool temperature to below 50 cP, thus helping to ensure full fiber wetting. CYCOM PR 520 RTM resin is fully cured following a 2-hour dwell at 180°C (355°F) after which it has a continuous hot/wet service temperature of 104°C (220°F). For reinforcement preforming operations, a fully compatible binder system, CYCOM® 7720 RTM, and a low areal weight film, PR 520-1, have been developed for use with CYCOM PR 520 RTM. The binder and low areal weight film are available pre-coated onto fabrics of the customer's choice. A separate datasheet for CYCOM 7720 RTM is available upon request. Suggested Applications: Engine Blades Engine Blade Spacers/Platforms Containment Cases Outer Guide Vanes Hinge/Brackets/Fittings

Message

CYCOM® PR 520 RTM is a one-part, 180°C (355°F) curing epoxy resin system offering superior damage tolerance and good strain to failure required for composite primary structure applications. The value of resin infusion is the ability to design complex geometric parts while leveraging a unitized structure which ultimately leads to a reduction in weight, lower part counts and the elimination of many post-manufacturing processes. CYCOM PR 520 RTM is an off-white thick paste at room temperature reducing to a low viscosity when heated for injection. The resin has a low enough viscosity to allow injection at 90 - 100°C (194 - 212°F). Following injection, the resin viscosity decreases with increasing tool temperature to below 50 cP, thus helping to ensure full fiber wetting. CYCOM PR 520 RTM resin is fully cured following a 2-hour dwell at 180°C (355°F) after which it has a continuous hot/wet service temperature of 104°C (220°F). For reinforcement preforming operations, a fully compatible binder system, CYCOM® 7720 RTM, and a low areal weight film, PR 520-1, have been developed for use with CYCOM PR 520 RTM. The binder and low areal weight film are available pre-coated onto fabrics of the customer's choice. A separate datasheet for CYCOM 7720 RTM is available upon request.

Suggested Applications:
Engine Blades
Engine Blade Spacers/Platforms
Containment Cases
Outer Guide Vanes
Hinge/Brackets/Fittings

General Information
Features	Good Toughness Heat Cure Low Moisture Absorption
Uses	Aerospace Applications Fittings Housings Structural Parts
Forms	Paste

Physical	Nominal Value	Unit
Specific Gravity ¹	1.25	g/cm³

Mechanical	Nominal Value	Unit
Tensile Modulus ²(24°C)	4000	MPa
Tensile Strength ³(24°C)	82.0	MPa
Tensile Elongation ⁴(Break)	3.0	%
Flexural Modulus ⁵	3450	MPa
Flexural Strength ⁶	153	MPa
Compressive Strength ⁷(24°C)	128	MPa
Shear Modulus ⁸	827	MPa
Shear Strength ⁹(24°C)	61.4	MPa

Thermal	Nominal Value	Unit
Glass Transition Temperature ¹⁰	161	°C

Note Message
1 .	Neat Resin
2 .	Neat Resin
3 .	Neat Resin
4 .	Neat Resin
5 .	Neat Resin
6 .	Neat Resin
7 .	Neat Resin
8 .	Neat Resin
9 .	Neat Resin
10 .	By DSC

Resin Grade	Manufacturer	Category	Trademark
RheTech Thermoplastic Polyolefin FT4702-527UV	RheTech, Inc.	Polyolefin, Unspecified	RheTech Thermoplastic Polyolefin
Viton® B-651C	DuPont Performance Elastomers	Fluorelastomer	Viton®
Chemlon® AF413	Teknor Apex Company (Chem Polymer)	Nylon 66	Chemlon®
Eco Cool Plus MP10	EcolBiotech Co., Ltd	PLA	Eco Cool Plus
Karina WHITE PVC COMPOUND 807D10/ 96-C-IS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina