LNP™ THERMOCOMP™ UF0069S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u1LH9t_LNP-THERMOCOMP-UF0069S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* UF0069S is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1006 FR HS LEX Product reorder name: UF0069S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.66 | g/cm³ | ASTM D792 |
| -- | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.59 | % | ISO 294-4 |
| Flow : 24 hr | 0.22 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.24 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13800 | MPa | ASTM D638 |
| -- | 12100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 182 | MPa | ASTM D638 |
| Break | 166 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.9 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12100 | MPa | ASTM D790 |
| -- | 12300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 258 | MPa | ASTM D790 |
| -- | 265 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 91 | J/m | ASTM D256 |
| 23°C 2 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 3 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 2.90 | J | ASTM D3763 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 299 to 310 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-320 | Teknor Apex Company | TPE | Medalist® |
| Vinnolit® S 4080 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| FHR Polypropylene 13T25A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| HiFill® PP GB40 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Romiloy® 9170 | ROMIRA GmbH | PC+ABS | Romiloy® |