Order Products : sales@su-jiao.com
INTEGRAL™ 801
| Category: | Polyolefin, Unspecified , Polyolefin Adhesive Film |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INTEGRAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u1GRdL_INTEGRAL-801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INTEGRAL™ 801 Film provides adhesion between substrates such as ABS and polystyrene at low processing temperatures. This product should be considered where temperature-sensitive substrates such as synthetic fabrics are involved. New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative. General Characteristics:
|
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Thickness - Recommended / Available | 1.0-2.0 mil (25-50 µ) | ||
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 51 µm | 123 | MPa | |
| 2% Secant, TD : 51 µm | 131 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 51 µm | 24.5 | MPa | |
| TD : Break, 51 µm | 14.5 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 51 µm | 400 | % | |
| TD : Break, 51 µm | 650 | % | |
| Dart Drop Impact (51 µm) | 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 190 | g | |
| TD : 51 µm | 340 | g | |
| Film Width | 50.80 to 167.64 | cm | |
| Peel Strength 1 | Internal Method | ||
| to ABS | 669.7 | g/2.5 cm | |
| to HIPS | 982.2 | g/2.5 cm | |
| to Polystyrene | 759.0 | g/2.5 cm | |
| Yield (25.0 µm) | 41.5 | m²/kg |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Activation Temperature | 71 | °C |
| Note Message | |
|---|---|
| 1 . | Heat seal testing at 300°F (149°C), 30 psi, (0.21 MPa), 1 second dwell. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Impact 8265 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| TPV Elastoprene® N55A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Trademark PE LLB1918C | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Geon™ Vinyl Flexible R1700E | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Kepex® 3300VS | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |