LNP™ THERMOCOMP™ WX88406 compound
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u07Lfl_LNP-THERMOCOMP-WX88406-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WX88406 is a compound based on PBT resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-W-88406 Product reorder name: WX88406 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7930 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break | 103 | MPa | |
| Break 2 | 103 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break | 2.9 | % | |
| Break 3 | 2.9 | % | |
| Flexural Modulus | ASTM D790 | ||
| -- | 7060 | MPa | |
| 50.0 mm Span 4 | 7060 | MPa | |
| Flexural Strength | ASTM D790 | ||
| -- | 165 | MPa | |
| Break, 50.0 mm Span 5 | 165 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 680 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 202 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UMG ALLOY® FA-840CD | UMG ABS, Ltd. | ASA+PC | UMG ALLOY® |
| Zytel® FG70G50HSLA BK309 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Edgetek™ AT-30GF/000 NC005 S-ROHS | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Geon™ Vinyl Flexible B85B0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina WHITE PVC COMPOUND 752D10/152-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |