NILFLEX® SH A0 MN001
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tzQZFZ_NILFLEX-SH-A0-MN001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEBS elastomer is the main consituent of these TPE-S (Thermoplastic Elastomer Styrenic) compounds. These compounds show high UV and ozone resistance. Nilflex SH is totally recyclable and it can be produced in standard grades and in tailor-made grades. Available in n atural, black and colored grade. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.870 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 380 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 0 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain | 0.0900 | MPa | |
| 300% Strain | 0.150 | MPa | |
| Tensile Strength 2(Break) | 2.35 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 1300 | % | ASTM D412 |
| Tear Strength | 10.0 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 110 to 160 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | Die C |
| 3 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 C 4230/100 GF10 MR20 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Daelim Po1y® LD-08A | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| DOWLEX™ NG 2038.11B | The Dow Chemical Company | LLDPE | DOWLEX™ |
| HiFill® ABS GF60 | Techmer Engineered Solutions | ABS | HiFill® |
| ICORENE® N6403 | A. Schulman Europe | PS (GPPS) | ICORENE® |