Ultramid® A3W
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tyiAv7_Ultramid-A3W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| An easy flowing, heat aging resistant injection moulding grade for fast processing. Uses include highly stressed parts such as bearings, bearing cages, gear-wheels, coil formers and cable connectors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 100 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 1.7 | -- | % | ISO 294-4 |
| Flow direction | 1.4 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.0 - 9.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 - 3.1 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 150 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.85 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature index- at 50% loss of tensile strength | IEC 60216 | |||
| -- 2 | 121 | -- | °C | IEC 60216 |
| -- 3 | 147 | -- | °C | IEC 60216 |
| Maximum operating temperature- short cycle operation | 200 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | -- | FMVSS 302 | |
| Polymer Abbreviation | PA66 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.4 | 20 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 25 | > 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus 4(1000 hr) | -- | 700 | MPa | ISO 899-1 |
| Flexural Modulus | 2900 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/A | |||
| -30°C | 6.0 | -- | kJ/m² | ISO 180/A |
| 23°C | 5.5 kJ/m² | No Break | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 7.0E-5 - 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1700 | -- | J/kg/°C | |
| Thermal Conductivity | 0.33 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+9 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.20 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 290 | °C | |
| Middle Temperature | 290 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 290°C, TW = 60°C |
| 2 . | 20000 h |
| 3 . | 5000 h |
| 4 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 3152 | Covestro - Polycarbonates | PC | Makrolon® |
| POLYNIL® C50 | Nilit Plastics | Nylon 66/6 | POLYNIL® |
| Propylux® CN-F | Westlake Plastics Company | PP, Unspecified | Propylux® |
| SureSpec HP-350 | Genesis Polymers | PP Homopolymer | SureSpec |
| Braskem PP TI6550WV | Braskem America Inc. | PP Impact Copolymer | Braskem PP |