PLUSTEK PA108
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tyX2ib_PLUSTEK-PA108.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GOOD SURFACE FINISH POLYAMIDE 6/6.6 ALLOY FOR INJECTION MOLDING APPLICATIONS. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.4 to 1.8 | % | ASTM D955 |
| -- | 1.4 to 1.8 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 8.5 | % | ASTM D570 |
| Saturation, 23°C | 8.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.8 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 90.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 140 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 45 | J/m | ASTM D256 |
| 23°C | 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648, ISO 75-2/A |
| Maximum Use Temperature - Short Peaks Operation | 150 | °C | |
| Maximum Continuous Use Temperature | 80 | °C | |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 120 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.60 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index | 750 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-6462 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Nypol® PA A3 G38 HS UV RH PRTA011 NR447 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Nylene® 5235 SP TF BK | Custom Resins Group | Nylon 6 | Nylene® |
| NYLAFORCE® B 50 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | NYLAFORCE® |
| Dryflex® 50670 | ELASTO | TPE | Dryflex® |