RTP 400 GB 20
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tyUPbS_RTP-400-GB-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4140 | MPa | ASTM D638 |
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength | 55.2 | MPa | ASTM D790 |
| Compressive Strength | 82.7 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 110 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 98.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 | |
| Arc Resistance | 75.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 4mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 204 - 288 | °C | |
| Middle Temperature | 204 - 288 | °C | |
| Front Temperature | 204 - 288 | °C | |
| Mold Temperature | 37.8 - 71.1 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer PP 408-401-P-10040-B | Polylink Polymers (India) Ltd. | XLPE | Polylink Polymer |
| Multi-Flex® TPE A7727 HM | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Cellophane™ 300P23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Diaterm® A27 GF30V0 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 6 | Diaterm® |
| Dryflex® SE 35A201 | ELASTO | TPE | Dryflex® |