PENTAMID A GV15 H RC black
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | txkPrq_PENTAMIDAGV15HRCblack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66, 15% glass fiber reinforced, Recompound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.4 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
| Viscosity Number | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5600 | 4400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 120 | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | 8.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 240 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 90 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.50 | -- | IEC 60250 | |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.2 mm) | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA66, MHRC, 14-060 N, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.070 - 0.15 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 265 - 285 | °C | |
| Middle Temperature | 270 - 295 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 265 - 295 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 69.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smooth-On MT-13® | Smooth-On, Inc | Epoxy | Smooth-On |
| Urochem 136 | Chemiplastica, Inc. | Urea Formald | Urochem |
| Elastron® V V601.A80.N | Elastron USA, Inc. | TPV | Elastron® V |
| LNP™ THERMOCOMP™ MF004AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| Durez® 33023 | SBHPP | Phenolic | Durez® |