WPP PP PPC2CF-2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tvVY1I_WPP-PP-PPC2CF-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Versions are available with various levels of copolymer to achieve desired levels of impact and modulus balance. Colors available meeting FDA requirements for food content applications. Compounds are offered with higher gloss. Note: Custom colors available upon request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 - 2.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 83 | ASTM D785 | |
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 18.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 440 | % | ASTM D638 |
| Flexural Modulus - Tangent | 986 | MPa | ASTM D790 |
| Flexural Strength | 30.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 40 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 190 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 1400 | J/m | ASTM D256 |
| Dart Drop Impact | ASTM D3029 | ||
| -30°C | 24.4 | J | ASTM D3029 |
| 23°C | 18.1 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 83.3 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 43.9 | °C | ASTM D648 |
| Additional Information |
|---|
| Flexural Modulus, ASTM D790, 2% Secant: 142000 psi |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 87.8 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 224 - 229 | °C | |
| Middle Temperature | 224 - 229 | °C | |
| Front Temperature | 227 - 232 | °C | |
| Nozzle Temperature | 232 - 243 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 4.14 - 7.58 | MPa | |
| Holding Pressure | 1.72 - 4.83 | MPa | |
| Back Pressure | 0.517 - 1.03 | MPa | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Speed: 1.5 to 2.5 in/sZone 4 Temperature: 450 to 460°FHot Runner Temperature: 450 to 480°FHydraulic Oil Temperature: 110 to 125°FShot Capacity vs. Barrel Capacity: 2.5 to 4Screw Decompression: 0.1 to 0.25 in |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANLENE® LDF 800GG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Haysite Plastics H232 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| LNP™ STAT-KON™ EE004 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| Plaskon 3400-2 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| LNP™ COLORCOMP™ MG38C compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |