Starex WR-9750H
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tvPGFs_Starex-WR-9750H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex WR-9750H is an Acrylonitrile Styrene Acrylate (ASA) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 39.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 75 | % | ASTM D638 |
| Flexural Modulus 3 | 1700 | MPa | ASTM D790 |
| Flexural Strength 4 | 52.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 95.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axpoly® r-PP51 1079 | Axion Polymers | PP Copolymer | Axpoly® |
| Ketron® PEEK-CA30 | Quadrant Engineering Plastic Products | PEEK | Ketron® |
| Huaxia Shenzhou PFA DS708-A | Shandong Huaxia Shenzhou New Material Co., Ltd. | PFA | Huaxia Shenzhou |
| Lionpol IM-40077 | Lion Polymers Incorporated | TPE | Lionpol |
| LG ABS HI121 | LG Chem Ltd. | ABS | LG ABS |