| 40 Shore D High Performance Polyester Elastomer |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 8.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 7.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.80 | % | |
| Water Absorption | |||
| 24 hr | 0.70 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 0.70 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 37 | ||
| Shore D, 15 sec | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 45.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 29.0 | MPa | |
| 10% Strain | 3.20 | MPa | |
| 50% Strain | 6.70 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 800 | % | ISO 527-2 |
| Flexural Modulus | 45.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 100 | kN/m | |
| Flow | 100 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -96.0 | °C | ISO 974 |
| Glass Transition Temperature 1 | -50.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 193 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.2E-4 | cm/cm/°C | |
| Transverse | 1.9E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.80 | ||
| 1 MHz | 4.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.013 | ||
| 1 MHz | 0.020 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Oxygen Index | 20 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.10 | g/cm³ |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission of Organic Compounds | 10.0 | µgC/g | VDA 277 |
| Odor | 4 | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SG840 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| FERREX® GPP35CG41UL WHITE | Ferro Corporation | PP Homopolymer | FERREX® |
| Kynar® 760 | Arkema | PVDF | Kynar® |
| Crastin® T843FR BK851 | DuPont Performance Polymers | PBT | Crastin® |
| Sylvin 9077A-70 White 125 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |