PEEK-OPTIMA® LT3
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Invibio Inc. |
| Trademark: | PEEK-OPTIMA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tuRCRe_PEEK-OPTIMA-LT3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEEK-OPTIMA® polymer from Invibio® is a high performance biomaterial providing advanced solutions for implant manufacturers. Formulated to meet the most exacting in-vivo criteria, PEEK-OPTIMA is biocompatible, safe and stable. Manufacturers of cardiovascular, dental, neurological and orthopaedic implants choose PEEK-OPTIMA for its:
Invibio offers a ‘no-change' agreement for the assured long-term supply of PEEK-OPTIMA. This guarantees its specification and production methods over an agreed period of time. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (210°C) | 1.3 | % | |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield 1 | 115 | MPa | |
| Yield | 108 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Break 2 | 20 | % | |
| Break | 25 | % | |
| Flexural Modulus | ISO 178 | ||
| -- 3 | 4000 | MPa | |
| -- | 4200 | MPa | |
| Flexural Stress 4 | 170 | MPa | ISO 178 |
| Compressive Stress | 135 | MPa | ISO 604 |
| Shear Modulus | 1000 | MPa | ISO 15310 |
| Shear Strength | 88.0 | MPa | ASTM D732 |
| Poisson's Ratio | 0.36 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -- 5 | 4.7 | kJ/m² | |
| -- | 4.5 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 340 | °C | |
| CLTE - Flow | ASTM D696 | ||
| -- 7 | 4.7E-5 | cm/cm/°C | |
| -- 8 | 1.1E-4 | cm/cm/°C | |
| RTI Elec | 260 | °C | UL 746 |
| RTI Imp | 260 | °C | UL 746 |
| RTI Str | 260 | °C | UL 746 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 9 | 1.60E-4 | MPa | Internal Method |
| Note Message | |
|---|---|
| 1 . | Rod |
| 2 . | Rod |
| 3 . | Rod |
| 4 . | Rod |
| 5 . | Rod |
| 6 . | Rod |
| 7 . | Below Tg |
| 8 . | Above Tg |
| 9 . | Capillary Rheometer |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delta IPP 14006 | Delta Polymers | PP Copolymer | Delta |
| Fainplast PVC FKA 89 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| HiFill FR® PA6 GF20 FR HS L | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| Kepex® 3830GF | Korea Engineering Plastics Co., Ltd | Polyester Alloy | Kepex® |
| OnFlex™ S EH 60A-3S7003 | PolyOne Corporation | TPE | OnFlex™ |