Menzolit® BMC 2310
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tuDzes_Menzolit-BMC-2310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® BMC 2310 is a bulk moulding compound based on unsaturated polyester resin. The product is reinforced with syntetic fibres and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor any heavy metals. Menzolit® BMC 2310 is a chemically resistant grade reinforced with special fibres. Being completely glass-free (no glass fibre reinforcement) it is specifically recommended for the manufacture of high voltage switchgear where SF6 is used to quench the arc. The specific fibre used is not affected by SF6 gas whereas glass fibre may erode away. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.18 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-4 |
| Tensile Stress (Break) | 20.0 | MPa | ISO 527-4 |
| Flexural Modulus | 10000 | MPa | ISO 14125 |
| Flexural Stress | 45.0 | MPa | ISO 14125 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | |
| Glass Transition Temperature | 165 | °C | ISO 11357-2 |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Arc Resistance | 185 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 36 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fiber Content | 9.0 | % | ISO 1172 |
| Material Designation | >UP-(MD+AF)91< | EN 14598-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 305 TFE 15 FR | RTP Company | PC | RTP |
| McCann PP M20CCPP10 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| Niblan VSF30 | Soredi S.p.a. | PBT | Niblan |
| LNP™ THERMOCOMP™ KF004A compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ THERMOCOMP™ |
| LNP™ LUBRICOMP™ KFP032 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |