FRAGOM XLC/900 OR
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ttlYVy_FRAGOM-XLC-900-OR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM G XLC/900 OR is a flame retardant halogen free polyolefin thermoplastic compound. FRAGOM G XLC/900 OR is a flexible flame retardant polyolefin thermoplastic compound having high temperature index and good oxygen index, suitable for OIL RESISTANT cable sheathing. Study to Crosslinking by radiations, to pass 30,000 cycles and Sadomaso test. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 33 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 60811 | ||
| Yield 1 | > 10.0 | MPa | |
| Yield 2 | > 5.00 | MPa | |
| Tensile Strain | IEC 60811 | ||
| Break 3 | > 150 | % | |
| Break 4 | > 250 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Stress 5(100°C, 24 hr, in IRM 902 Oil) | < 20 | % | IEC 60811 |
| Change in Tensile Strain at Break 6(100°C, 24 hr, in IRM 902 Oil) | < 20 | % | IEC 60811 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | ASTM D2863 | ||
| -- 7 | 38 | % | |
| -- 8 | 36 | % | |
| Corrosive Gas in Smoke - pH | > 4.50 | IEC 60754-2 | |
| Halogen Content | < 0.300 | % | IEC 60754-1 |
| Temperature Index (Burning) 9 | 300 | °C | NES 715 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 120 | °C | |
| Cylinder Zone 2 Temp. | 135 | °C | |
| Cylinder Zone 3 Temp. | 150 | °C | |
| Cylinder Zone 4 Temp. | 165 | °C | |
| Cylinder Zone 5 Temp. | 170 | °C | |
| Die Temperature | 175 | °C |
| Note Message | |
|---|---|
| 1 . | After Crosslinking |
| 2 . | Before Crosslinking |
| 3 . | After Crosslinking |
| 4 . | Before Crosslinking |
| 5 . | After Crosslinking |
| 6 . | After Crosslinking |
| 7 . | After Crosslinking |
| 8 . | Before Crosslinking |
| 9 . | 21% O2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN0320SN02 | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| Vydyne® 22HSP | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| YUPLENE® H230PL | SK Global Chemical | PP Homopolymer | YUPLENE® |
| Elastollan® 1185A50X | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Karina CLEAR PVC COMPOUND 78/202-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |