LNP™ THERMOCOMP™ DX13354X compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ttR0vz_LNP-THERMOCOMP-DX13354X-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Thermocomp* compound DX13354X is a colorable, glass fiber reinforced Polycarbonate resin based LDS material solution with stable plating and RF performance, providing excellent stiffness with good surface and good impact strength. The product is available for internal and external parts for Laser Direct Structuring applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 280°C/2.16 kg | 12 | g/10 min | |
| 300°C/1.2 kg | 16 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 13.0 | cm³/10min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6900 | MPa | ASTM D638 |
| -- | 6600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 90.0 | MPa | ASTM D638 |
| Break | 90.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 3 | 2.2 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 6300 | MPa | ASTM D790 |
| -- | 6400 | MPa | ISO 178 |
| Flexural Strength | 130 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 36 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C | 90 | J/m | ASTM D256 |
| 23°C 4 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 500 | J/m | ASTM D4812 |
| 23°C 5 | 32 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 124 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 6 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 122 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | Internal Method | ||
| 1.10 GHz | 3.48 | ||
| 1.90 GHz | 3.46 | ||
| 5.00 GHz | 3.45 | ||
| Dissipation Factor | Internal Method | ||
| 1.10 GHz | 0.013 | ||
| 1.90 GHz | 0.012 | ||
| 5.00 GHz | 0.011 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 270 to 295 | °C | |
| Middle Temperature | 270 to 295 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 100 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CelloTherm™ P400 | Innovia Films Ltd. | CA | CelloTherm™ |
| Chiao Fu PA66 MD212LST NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Chemical Resources PMMA600 | Chemical Resources, Inc. | Acrylic (PMMA) | Chemical Resources |
| Leona™ CR301 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Karina BLACK PVC COMPOUND 450-48/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |