Order Products : sales@su-jiao.com
Impet® 330R
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Impet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ttLvYD_Impet-330R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impet 330R is a 30% glass reinforced injection moldable polyester containing post consumer recycled PET. It provides an excellent combination of strength, stiffness, and high temperature resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.70 | % | ASTM D955 |
| Vertical flow direction | 0.60 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.16 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11100 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 165 | MPa | ASTM D638 |
| Fracture | 159 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture | 2.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 229 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.8 | kJ/m² | ISO 179/1eA |
| 23°C | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 28 | kJ/m² | ISO 179/1eU |
| 23°C | 27 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 224 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 221 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 73.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 244 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 3.1E+14 | ohms | ASTM D257 |
| -- | 3.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 3.0E+15 | ohms·cm | ASTM D257 |
| -- | 7.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 22 | kV/mm | ASTM D149 |
| -- | 32 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.20 | ASTM D150 | |
| 10 kHz | 3.10 | ASTM D150 | |
| 100 Hz | 2.83 | IEC 60250 | |
| 1 MHz | 3.46 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 0.010 | ASTM D150 | |
| 10 kHz | 0.016 | ASTM D150 | |
| 100 Hz | 0.012 | IEC 60250 | |
| 1 MHz | 0.014 | IEC 60250 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index | 175 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 255 - 265 | °C | |
| Middle Temperature | 260 - 275 | °C | |
| Front Temperature | 260 - 275 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 110 - 121 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 260 to 290°CZone 4 Temperature: 265 to 280°CFeed Temperature: 255 to 265°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProvaMed® PVC 2278 | ACTEGA GmbH | PVC, Unspecified | ProvaMed® PVC |
| Sinvicomp DBS3025 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| VITAMIDE® BI72NT6506 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| LUVOCOM® 1-8501 | LEHVOSS Group | Nylon 66 | LUVOCOM® |
| INEOS LDPE 20N430 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |