Badamid® LA70 GF50 HH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ttGv1e_Badamid-LA70-GF50-HH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66-GF50 50% glass fibres reinforced injection moulding grade, heat stabilized, for technical products with high thermal resistance and high stiffness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 3.7 to 4.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.0 to 1.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16500 | 12500 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 230 | 180 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 2.5 | 3.5 | % | ISO 527-2/5 |
| Flexural Stress 3(23°C) | 360 | 300 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | |||
| -30°C | 13 | -- | kJ/m² | |
| 23°C | 17 | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | 85 | -- | kJ/m² | |
| 23°C | 95 | 100 | kJ/m² | |
| Notched Izod Impact Strength 6(23°C) | 13 | 15 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 260 | -- | °C | ISO 3146 |
| CLTE 9 | DIN 53752 | |||
| Flow | 5.0E-6 to 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 to 6.0E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 140 | -- | °C | |
| some hours | 240 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 10 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 11 | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity 12(1 MHz) | 3.80 | 6.60 | IEC 60250 | |
| Dissipation Factor 13(1 MHz) | 0.015 | 0.17 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating 14(1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4 mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | >=10x10x4 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA B3 G10 V10 NTLA010 NT309 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| FLEXCHEM™ 8552 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| EMERGE™ PC/ABS 7100 | Trinseo | PC+ABS | EMERGE™ |
| Kumho ABS 780F | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Sylvin 9058-90UV Orange 538 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |