Tritheva® TN 2020
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Tritheva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tt8HQD_Tritheva-TN-2020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tritheva®TN 2020 is an ethylene vinyl acetate copolymer (EVA) material,. This product is available in Latin America and is processed by film extrusion or co-extrusion. Tritheva®The main features of TN 2020 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.931 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 8.0 - 9.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 7.00 | MPa | ASTM D638 |
| Fracture, molding | 19.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 700 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 67.0 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 64.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 22.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 490 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 730 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 79.0 | °C | ASTM D1525 |
| Melting Temperature | 100 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45, 50.0 µm, blown film | 86 | ASTM D2457 | |
| 60, 50.0 µm, blown film | 140 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 1.8 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 1.7 to 2.3 g/10 min |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 - 140 | °C | |
| Cylinder Zone 2 Temp. | 135 - 150 | °C | |
| Cylinder Zone 3 Temp. | 145 - 165 | °C | |
| Adapter Temperature | 165 - 185 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® MR | Röchling Engineering Plastics SE & Co. KG | UHMWPE | POLYSTONE® |
| Ateva® 2842A | Celanese EVA Performance Polymers | EVA | Ateva® |
| Karina BLACK PVC COMPOUND TR-602D48/ 1-Y-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PA840G7 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Enable™ 35-05HH | ExxonMobil Chemical | mPE | Enable™ |