Asaflex™ 835
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Asaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tt7lNI_Asaflex-835.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sheet extrusion grade. Blended with SC*, for sheets with high transparency and high impact resistance. It is supplied in pellet form. In blends with GPPS, for dessert cups. In blends with SC, for blister packs and shrink films with high transparency and high impact strength. * Styrenic copolymer from PS Japan Corp. similar to Asaflex™ 835 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS (general-purpose polystyrene). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 10 | ISO 2039-2 | |
| Shore Hardness (Shore D) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 250 | % | ISO 527-2/5 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Flexural Stress | 21.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Partial Break) | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 72.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 89.0 | % | ISO 3537 |
| Haze (2000 µm) | 2.0 | % | ISO 3537 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® M-532 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| Celstran® PP-GF30-0455 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Hyosung Polyketone M730A | Hyosung Corporation | PK-Aliphatic | Hyosung Polyketone |
| LNP™ THERMOTUF™ V1000SU compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOTUF™ |
| ICORENE® 1210 | A. Schulman Europe | LLDPE | ICORENE® |