Elastollan® 880A-13N
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tslURh_Elastollan-880A-13N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® 880AN is specifically formulated for transparent film applications. It exhibits excellent abrasion resistance, toughness, transparency, and oil/fuel resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan®880AN is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/3.8 kg | 15 to 25 | g/10 min | |
| 190°C/8.7 kg | 40 to 60 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 24.8 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 22.1 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 40.0 | mg | ASTM D1044 |
| Abrasion - DIN | 10 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 66 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 5.31 | MPa | |
| 300% Strain | 12.7 | MPa | |
| Tensile Strength | 33.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 610 | % | ASTM D412 |
| Tear Strength 1 | 85.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | |
| 70°C, 22 hr | 50 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -27.0 | °C | Internal Method |
| Vicat Softening Temperature | 64.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 125577 | RTP Company | Nylon 6 | RTP |
| Stat-Rite® M809 | Lubrizol Advanced Materials, Inc. | Acrylic, Unspecified | Stat-Rite® |
| TOTAL Polyethylene HDPE HL 428 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| Karina BROWN COLOR CONCENTRATE -E 36/339-RG-G | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 7833-85 Yellow 4113 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |