Order Products : sales@su-jiao.com

Sumitomo PP AZ564

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	Sumitomo Chemical Asia
Trademark:	Sumitomo PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	tsZDFM_Sumitomo-PP-AZ564.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
BlockCopolymer,InjectionMolding

General Information
Additive	Nucleating Agent
Features	Block Copolymer High Flow High Heat Resistance High Impact Resistance High Stiffness
Uses	Appliance Components Appliances Automotive Applications Crates Household Goods
Agency Ratings	FDA 21 CFR 177.1520(c) 3.1a
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.900	g/cm³	ASTM D792A
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	30	g/10 min	ASTM D1238
Molding Shrinkage			Internal Method
Across Flow	1.4	%
Flow	1.4	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness	90		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	24.0	MPa
Break	17.0	MPa
Flexural Modulus	1290	MPa	ASTM D790A

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength			ASTM D256
-20°C	5.0	kJ/m²
23°C	8.0	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	109	°C	ASTM D648
Vicat Softening Temperature	151	°C	ASTM D1525 ¹

Injection	Nominal Value	Unit
Processing (Melt) Temp	190 to 230	°C
Mold Temperature	20.0 to 70.0	°C

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
RTP ESD A 905	RTP Company	PSU	RTP
Witcobond® W-281F	Chemtura	PUR-Ester	Witcobond®
Later 4-V0HF1	LATI S.p.A.	PBT	Later
Karina BLACK PVC COMPOUND 70900-48/1-E-AC	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Plenco 04309 (Injection)	Plastics Engineering Co.	Phenolic	Plenco