ULTEM™ 2300F resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | trR1ss_ULTEM2300Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. US FDA and European Food Contact compliant. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU2300. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.90 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 165 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 165 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8500 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 20.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | ISO 180/1U |
| 23°C | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 215 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 210 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 225 | °C | ISO 306/A50 |
| -- | 213 | °C | ISO 306/B50 |
| -- | 220 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.29 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.6E-3 | IEC 60250 | |
| 60 Hz | 1.6E-3 | IEC 60250 | |
| 1 MHz | 2.3E-3 | IEC 60250 | |
| 2.45 GHz | 5.3E-3 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 150 | V | IEC 60112 |
| Solution B | 100 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 48 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 350 - 400 | °C | |
| Middle Temperature | 360 - 410 | °C | |
| Front Temperature | 370 - 420 | °C | |
| Nozzle Temperature | 360 - 410 | °C | |
| Processing (Melt) Temp | 370 - 410 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® 3007C Opaque | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Selvol™ 165 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Naxel PC30 | Custom Resins Group | PC | Naxel |
| NuSil MED-6342 | NuSil Technology | Silicone | NuSil |
| Latilub 73/13-10ST | LATI S.p.A. | Acetal (POM) Copolymer | Latilub |