DOWLEX™ SC 2111G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | trQeL6_DOWLEX-SC-2111G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™SC 2111G polyethylene resin is specially used in large/high-yield cast film production lines to prepare high-performance industrial stretched films. The film prepared by DOWLEX SC 2111G polyethylene resin has excellent balance in processing properties, mechanical properties and tensile properties. DOWLEX SC 211G polyethylene resin is used as a core layer resin in the co-extrusion cast film structure, and a self-adhesive resin is co-extruded to prepare a film with a thickness between 10 and 35 microns. When used in the application field of food contact, DOWLEX SC 211G polyethylene resin should comply with the requirements of the U.S. Food and Drug Administration Regulation 21 CFR 177.1520 and the requirements of the food contact regulations of most European countries without modification and when the processing process follows the requirements of good manufacturing practices. Please contact your nearest Dow representative for proof of compliance with the Food Contact Act. The purchaser remains responsible for determining whether the use of its products complies with all relevant regulations. Application field:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.7 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Puncture Force 1(23 µm) | 31.0 | N | Internal method |
| Tensile Stress 2 | ISO 527-3 | ||
| MD : Yield, 23 µm | 5.80 | MPa | ISO 527-3 |
| TD : Yield, 23 µm | 6.00 | MPa | ISO 527-3 |
| MD : Break, 23 µm | 34.0 | MPa | ISO 527-3 |
| TD : Break, 23 µm | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation 3 | ISO 527-3 | ||
| MD : Break, 23 µm | 430 | % | ISO 527-3 |
| TD : Break, 23 µm | 690 | % | ISO 527-3 |
| Dart Drop Impact 4(23 µm) | 110 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 23 µm | 170 | g | ASTM D1922 |
| TD : 23 µm | 550 | g | ASTM D1922 |
| Film tensile properties-maximum tensile force | 36000 | g | Internal method |
| Film Tensile Properties-Maximum Elongation | 350 | % | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 6(45°, 23.0 µm) | 93 | ASTM D2457 | |
| Haze 7(23.0 µm) | 0.60 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 冷却辊温度：25°C 熔体温度：250°C 建议的厚度范围：10 至 35 µm |
| Note Message | |
|---|---|
| 1 . | Cast film manufactured at 250 m/min. |
| 2 . | Cast film manufactured at 250 m/min. |
| 3 . | Cast film manufactured at 250 m/min. |
| 4 . | Cast film manufactured at 250 m/min. |
| 5 . | Cast film manufactured at 250 m/min. |
| 6 . | Cast film manufactured at 250 m/min. |
| 7 . | Cast film manufactured at 250 m/min. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPV Elastoprene® N80A-i | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Hostacom TKC 782N | LyondellBasell Industries | TPO (POE) | Hostacom |
| Petrothene® NA285003 | LyondellBasell Industries | MDPE | Petrothene® |
| TOTAL Polypropylene Aceso® PPM H250 S01 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Sylvin 9604A-80 Clear 8159 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |