EPO-TEK® H20E-SLR-HVMX
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tr2Eex_EPO-TEK-H20E-SLR-HVMX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® H20E-SLR-HVMX is a two-component, electrically conductive, epoxy for meter mix dispensing applications. It is designed for solar ribbon bonding of photovoltaic modules. It provides the electrical back-contact for ribbon stringing of solar cells into modules and panels. It is a higher viscosity version of EPO-TEK H20E-SLR-MX. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 400 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus | 6.11 | GPa | |
| Thixotropic Index | 3.51 | ||
| Weight Loss on Heating | |||
| 200°C | 0.36 | % | |
| 250°C | 1.3 | % | |
| 300°C | 2.4 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | 88.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.1E-5 | cm/cm/°C | |
| -- 3 | 2.6E-4 | cm/cm/°C | |
| Thermal Conductivity | 1.5 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 11 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Amber | ||
| -- 5 | Silver | ||
| Density | |||
| Part B | 1.10 | g/cm³ | |
| Part A | 2.60 | g/cm³ | |
| Viscosity 6(23°C) | 7.2 | Pa·s | |
| Curing Time (140°C) | 0.17 | hr | |
| Pot Life | 1100 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 55 | ||
| Lap Shear Strength (23°C) | 12.7 | MPa | |
| Volume Resistivity (23°C) | < 4.0E-3 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tool-A-Thane UT-405 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| ALCOM® PA66 910/1 GF30 MO1 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Geon™ Vinyl Flexible XV3855 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| KOPLA PA66 KDG1080 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Sylvin 9067-65 Brown 7403 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |