DOWLEX™ 2606 GC
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tqeRxM_DOWLEX-2606-GC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX 2606 GC Polyethylene Resinis specifically designed for large/high output cast film lines to make high performance industrial stretch films. Films made from DOWLEX 2606 GC exhibit an excellent balance of processability, mechanical and stretchability performance properties. DOWLEX 2606 GC Polyethylene Resin is to be used as a core resin in coextruded cast film structures for films in the thickness range between 10 and 35 microns. Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Puncture Energy (23 µm) | 133 | J | |
| Film Puncture Force (23 µm) | 31.0 | N | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 23 µm | 6.00 | MPa | ASTM D882 |
| TD : Yield, 23 µm | 6.00 | MPa | ASTM D882 |
| MD : Break, 23 µm | 36.0 | MPa | ASTM D882 |
| TD : Break, 23 µm | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 23 µm | 400 | % | ASTM D882 |
| TD : Break, 23 µm | 680 | % | ASTM D882 |
| Dart Drop Impact (23 µm) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 23 µm | 150 | g | ASTM D1922 |
| TD : 23 µm | 450 | g | ASTM D1922 |
| Film tensile properties-maximum tensile force (23.0 µm) | 36000 | g | Internal method |
| Film Tensile Properties-Maximum Elongation (23.0 µm) | 350 | % | Internal method |
| Additional Information |
|---|
| Film Properties: Cast Film fabrication at 250 m/min. |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film Extrusion: Chill Roll Temperature: 20 - 40°C Melt Temperature: 220 - 280°C Recommended Gauge Range: 10 - 35 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® 3017IR | Samyang Corporation | PC | TRIREX® |
| Andur M-22 (DEG) | Anderson Development Company | PUR-Ester/MDI | Andur |
| IROGRAN® A 92 E 4246 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LONGLITE® PBT 3030-200S | CCP Group | PBT | LONGLITE® PBT |
| TechnoDur PBT2 FR Natural (9984) | TechnoCompound GmbH | PBT | TechnoDur |