Order Products : sales@su-jiao.com
SABIC® PPcompound G3230A
| Category: | PP, Unspecified , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tqGsRg_SABIC-PPcompound-G3230A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound G3230A is a 30% short glass fiber reinforced Polypropylene for unter-the-hood and structural applications. The base material is a PP homopolymer and is available in standard black. The glass fibres are chemically coupled to the PP matrix. This material has been designed to combine a good performance profile with fast processing. SABIC® PPcompound G3230A is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 7150 | MPa | ISO 527-2/1A/5 |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 93.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(Injection Molded) | 6900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 48 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C, Injection Molded) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 150 | °C | ISO 75-2/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 4.0E-5 | cm/cm/°C | |
| 23 to 80°C | 4.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 3-point loading |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 80207 EM HS | RTP Company | Nylon 66 | RTP |
| ShinkoLite-P IR D-30 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Next Nylon 6 Prime Series NX-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| LEXAN™ 105 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 2960-80 White 1500 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |