Rilsan® BMNO SG FILAGE
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tpgNnO_Rilsan-BMNO-SG-FILAGE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BMNO SG FILAGE is a polyamide 11 produced from a renewable source. This natural grade is particularly suitable for textile applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 0.80 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 75 | ||
| Shore D, 15 sec | 68 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1280 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 41.0 | MPa | |
| Break | 58.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 1140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 189 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, M, 12-010 | ISO 1874 | |
| Renewable Carbon Conent | 100 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 240 to 270 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® PP HLS-080SP | Saudi Polymers Company | PP Homopolymer | Marlex® PP |
| Sylvin 8724-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Europrene Latice® CC 136 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Fainplast PVC FK 93 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LNP™ STAT-KON™ AD000Z compound | SABIC Innovative Plastics | ABS | LNP™ STAT-KON™ |