GELOY™ CR8510 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tofLCy_GELOYCR8510resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 6.3 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 11 | g/10 min | ASTM D1238 |
| 280°C/3.8 kg | 7.8 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 6.00 | cm³/10min | ISO 1133 |
| 260°C/5.0 kg | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1970 | MPa | ASTM D638 |
| -- 2 | 2080 | MPa | ASTM D638 |
| -- | 2040 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 40.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 33.0 | MPa | ASTM D638 |
| Fracture | 19.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 3.6 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2/50 |
| Fracture 6 | 60 | % | ASTM D638 |
| Fracture | 35 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2170 | MPa | ASTM D790 |
| -- 8 | 2060 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 64.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 23°C | 400 | J/m | ASTM D256 |
| -30°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 15 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 4.00 | J | ASTM D3763 |
| 23°C, Total Energy | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 103 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 13 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 14 | 88.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 15 | 89.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525 16 |
| -- | 102 | °C | ISO 306/B50 |
| -- | 105 | °C | ISO 306/B120 |
| Ball Pressure Test 17(98°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dissipation Factor | ASTM D150 | ||
| 100 kHz | 0.018 | ASTM D150 | |
| 1 MHz | 0.026 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 94 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 215 - 250 | °C | |
| Middle Temperature | 220 - 255 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Nozzle Temperature | 220 - 255 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 60.0 - 85.0 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa | |
| Screw Speed | 30 - 80 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | 120*10*4 mm |
| 15 . | 80*10*4 mm |
| 16 . | 标准 B (120°C/h), 载荷2 (50N) |
| 17 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LMP322 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Sinvicomp SIG5001 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TABOND 5007 | SILON s.ro | PP, Unspecified | TABOND |
| Forprene® 6NM901A65 | SO.F.TER. SPA | TPV | Forprene® |
| INNOPOL® PP CS 1-4940 MC | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |