Halene H B6001L
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tnfySl_Halene-H-B6001L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
B6001L is a Blow Molding Grade HDPE produced by the Spherilene Technology. This resin is particularly recommended for upto 20-liter containers for Lubricants and Edible oils. B6001L combines exceptional processability with high rigidity, excellent mechanical properties and impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Compression Molded) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | > 900 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1300 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 350 | J/m | ASTM D256A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 165 | °C | |
| Cylinder Zone 4 Temp. | 175 | °C | |
| Die Temperature | 180 - 185 | °C |
| Extrusion instructions |
|---|
| Parison Temperature: 185-190°CCooling Water for Mold: 20-25°C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SV-17500U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| TRIPET® 2550GN40 | Samyang Corporation | PET | TRIPET® |
| NORYL™ WCV065 resin | SABIC Innovative Plastics | PPE+Polyolefin | NORYL™ |
| Ateva® 1609 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Jackdaw PC DR14NT6731 | Jackdaw Polymers | PC | Jackdaw PC |